Laser induction hybrid rapid cladding of WC particles reinforced NiCrBSi composite coatings

In order to investigate the microstructure characteristics and properties of Ni-based WC composite coatings containing a relatively large amount of WC particles by laser induction hybrid rapid cladding (LIHRC) and compare to the individual laser cladding without preheating, Ni60A + 35 wt.% WC composite coatings are deposited on A3 steel plates by LIHRC and the individual laser cladding without preheating. The composite coating produced by the individual laser cladding without preheating exhibits many cracks and pores, while the smooth composite coating without cracks and pores is obtained by LIHRC. Moreover, the cast WC particles take on the similar dissolution characteristics in Ni60A + 35 wt.% WC composite coatings by LIHRC and the individual laser cladding without preheating. Namely, the completely dissolved WC particles interact with Ni-based alloy solvent to precipitate the blocky and herringbone carbides, while the partially dissolved WC particles still preserve the primary lamellar eutectic structure. A few WC particles are split at the interface of WC and W2C, and then interact with Ni-based alloy solvent to precipitate the lamellar carbides. Compared with the individual laser cladding without preheating, LIHRC has the relatively lower temperature gradient and the relatively higher laser scanning speed. Therefore, LIHRC can produce the crack-free composite coating with relatively higher microhardness and relatively more homogeneous distribution of WC particles and is successfully applied to strengthen the corrugated roller, showing that LIHRC process has a higher efficiency and good cladding quality.