Studies of intrawall porosity in the hexagonally ordered mesostructures of SBA-15 by small angle X-ray scattering and nitrogen adsorption

Ordered mesoporous silicas (OMSs) such as SBA-15 (p6mm symmetry group) synthesized in the presence of block copolymers containing poly(ethylene oxide) blocks possess irregular complementary pores in the walls of ordered mesopores. The X-ray scattering caused by this complementary porosity contributes to the background of the SAXS patterns. This work shows the possibility of using the SAXS data for the study of intrawall channels interconnecting ordered cylinders in SBA-15. The proposed SAXS analysis was tested by using a series of SBA-15 samples obtained at different temperatures of hydrothermal treatment (from 60 to 180 °C). The structural modelling of the SAXS patterns recorded for a series of SBA-15 samples was performed by using the continuous density function (CDF) technique in combination with the derivative difference minimization (DDM) method of full-profile refinement. This method is well suited for extraction of the background curves from the SAXS patterns. The resulting smooth background curves were analyzed by the well-known method in the SAXS theory used for evaluation of heterogeneity distributions, which in this case characterize the intrawall complementary porosity. A relatively good agreement has been observed between the data obtained by SAXS and nitrogen adsorption analysis. The SAXS analysis is sufficiently sensitive for examination of heterogeneous microporosity in SBA-15 materials. The average diameter of intrawall pores for the SBA-15 sample obtained at 60 °C was only about 1.4 nm. However, this diameter increased with the increasing temperature of hydrothermal treatment; namely, it was 1.5, 1.8, 2.6, 2.6, 3.5 and 5.2 nm for the SBA-15 samples hydrothermally treated at 80, 100, 120, 140, 160 and 180 °C, respectively.