Fabrication of triazinedithiol functional polymeric nanofilm by potentiostatic polymerization on aluminum surface Review Article

The functional polymeric nanofilm of 6-(N-allyl-1,1,2,2-tetrahydroperfluorodecyl)amino-1,3,5-triazine-2,4-dithiol monosodium (AF17N) was prepared on pure aluminum surface by potentiostatic polymerization at different potentials. The thickness and weight of polymeric nanofilm increased proportionally to electro-polymerization potential following linear equation. The chemical structure of nanofilm was characterized by Fourier transform-infrared (FT-IR) spectroscopy and X-ray photoelectron spectroscopy (XPS). Adsorption peaks in FT-IR and C1s, N1s, S2p, F1s and Al2p peaks in XPS spectra indicated that the polymeric nanofilm was poly(6-(N-allyl-1,1,2,2-tetrahydroperfluorodecyl)amino-1,3,5-triazine-2,4-disulfide) (PAF17). The morphologies of polymeric nanofilm were also observed by atomic force microscopy (AFM). All the results showed that the optimal electro-polymerization potential and time were 8 V and 20 s, respectively. Uniform and compact nanofilm of PAF17 could be obtained under these conditions. It is expected that this technique will be applied in the preparation of lubricating, dielectric and hydrophobic surface on aluminum substrate.