Model calculation of the surface tension of liquid Ga–Bi alloy

A convenient model, based on some assumptions, for calculating the composition and temperature dependence of the surface tension of binary liquid alloys is reported. The theoretical calculations of the surface tension of gallium-rich-bismuth alloys are presented. The calculated results are compared with the reported experimental data. A relatively good agreement with experimental behavior of the composition dependence of the surface tension was found, but a disagreement was observed with experimental temperature behavior of the surface tension of these alloys. The calculations were conducted in the temperature range from almost 320 K to about 800 K. The surface tension was calculated from eutectic composition (xBi = 0.0022) to xBi = 0.1, and worked out by linear equations. The model calculation and analysis indicate a first order surface phase transition in this system, which is in accord with experimental findings. For this system, γ decreases linearly with increasing temperature at fixed Bi mole fraction xBi, and thus, suggesting a positive surface excess entropy. It is also found that the surface tension isotherms show the linear dependence on the concentration, in the logarithm scale of xBi, in the very narrow concentration range.