The improvement of moisture resistance and thermal stability of Ca3SiO4Cl2:Eu2+ phosphor coated with SiO2

Green-emitting phosphors Ca3SiO4Cl2:Eu2+ were prepared by the high temperature solid-state method. Sol–gel process was adopted to encapsulate the as-prepared phosphors with tetraethylorthosilicate (TEOS) as silicon coating reagent. Fluorescence spectrometer, scanning electron microscopy (SEM) and powder X-ray diffraction (XRD) patterns were employed to characterize the emission spectra, the surface morphologies and the phase structures, respectively. The chemical stability testing was operated by the method of soaking the phosphors in deionized water and roasting them at different temperatures. The results indicated that the surfaces of the green phosphors were evenly coated by SiO2 and the phase structure of the coated phosphors remained the same as the uncoated samples. The luminance centre of Eu2+ did not shift after surface treatment and the luminance intensity of coated phosphors was lower than that of the uncoated samples. The results demonstrated that the water-resistance stability of the coated phosphor was improved to some degree because the pH value and the luminance intensity variation were both smaller than the uncoated phosphor after steeping within the same time. Moreover, the thermal stability of coated phosphors was enhanced obviously compared to the original samples based on the temperature dependent emission spectra measurement.