Surfactant assisted synthesis of lamellar nanostructured LiFePO4 at 388 K

Lamellar nanostructured lithium iron phosphate (Lα-LFP) was synthesized using anion surfactant sodium dodecyl sulphonate (SDS) as supermolecular template in water–ethanol media at 388 K under self-generated pressure. FeSO4, (NH4)2HPO4 and LiOH were used as Fe, P and Li sources, respectively. The inorganic phase was analyzed by X-ray diffraction (XRD). The morphology and the lamellar nanostructure were observed by field emitting scanning electron microscopy (FESEM). The results showed that the synthesized Lα-LFP presents not only the ordered lamellar microstructure accumulated by 20–40-nm thick LFP layers, but also the consequent self-assembled blocky particles of 0.5–1 μm. In contrast, template free LFP (TF-LFP) show a flake-shaped and mess-orientated microstructure. As a soft template, SDS played the roles of inducing the lamellar nanostructure, purifying the inorganic phase and decreasing the synthesis temperature.