Fabrication of superhydrophobic binary nanoparticles/PMMA composite coating with reversible switching of adhesion and anticorrosive property

Ag–TiO2–Thiol/Poly(methyl methacrylate) (PMMA) coating has been prepared via adsorbed-layer nanoreactor technique and self-assembling method. The composite coating shows a superhydrophobic property with reversible switching of adhesion. In the UV–vis spectra, absorption appeared in ultraviolet region of 229–293 nm (UVC region) and 320–370 nm (UVA region). Additionally, the stability of the superhydrophobic surface was tested under the following conditions: (1) in basic solution (pH = 14); (2) in acid solution (pH = 1); (3) in artificial seawater. The coating shows stability since the contact angle of the sample still remained higher than 150° in the above conditions. The corrosion resistance of the superhydrophobic surfaces was investigated by electrochemical measurements and the results revealed that the superhydrophobic coatings are anticorrosive well.