Solid-state pH nanoelectrode based on polyaniline thin film electrodeposited onto ion-beam etched carbon fiber Original Research Article

An ultramicro pH sensor has been constructed based on a thin polyaniline film that was electrochemically deposited onto a carbon fiber nanometer-size electrode. The substrate nanoelectrodes were fabricated using ion-beam conically etched carbon fibers with tip diameters ranging ca. from 100 to 500 nm. The polyaniline film was deposited from HCl solution containing the aniline monomer by cycling the potential between −0.2 and +1.0 V. The electromotive force (emf) signal between the pH sensitive polyaniline-coated nanoelectrode and an Ag/AgCl reference electrode was linear over the pH range of 2.0–12.5 with a slightly super-Nernstian slope of ca. −60 mV/pH unit. Response times ranged from several sec at pHs around 7 up to 2 min at pH 12.5. The proposed pH nanoelectrode displayed high ion selectivity with respect to K+, Na+, Ca2+, and Li+, with log KH,M values around −12 and has a working lifetime of about 20 days. Key parameters important for the pH nanoelectrode performance, including polyaniline film preparation, selectivity, response time, temperature dependence, relative coating thickness, stability, and reproducibility, have been characterized and optimized. The performance of the pH nanoelectrode was examined by measuring the pH of several real samples including body fluids (serum, urine) and low ionic strength water samples (rain, deionized and tap water). The results agreed very well with those obtained by using commercial glass pH electrodes. The proposed pH nanoelectrode demonstrated attractive properties and seems particularly promising for use under physiological conditions.