Preparation and evaluation of graphene-coated solid-phase microextraction fiber Original Research Article

In this paper, a novel graphene (G) based solid-phase microextraction (SPME) fiber was firstly prepared by immobilizing the synthesized G on stainless steel wire as coating. The new fiber possessed a homogeneous, porous and wrinkled surface and showed excellent thermal (over 330 °C), chemical and mechanical stability, and long lifespan (over 250 extractions). The SPME performance of the G-coated fiber was evaluated in detail through extraction of six pyrethroid pesticides. Although the thickness of G-coated fiber was only 6–8 μm, its extraction efficiencies were higher than those of two commercial fibers (PDMS, 100 μm; PDMS/DVB, 65 μm). This high extraction efficiency may be mainly attributed to huge delocalized π-electron system of G, which shows strong π-stacking interaction with pyrethroid pesticide. The G-coated fiber was applied in the gas chromatographic determination of six pyrethroids, and their limits of detection were found to be ranged from 3.69 to 69.4 ng L−1. The reproducibility for each single fiber was evaluated and the relative standard deviations (RSDs) were calculated to be in the range from 1.9% to 6.5%. The repeatability of fiber-to-fiber and batch-to-batch was 4.3–9.2% and 4.1–9.9%. The method developed was successfully applied to three pond water samples, and the recoveries were 83–110% at a spiking of 1 μg L−1.