A nanoindentation analysis of the effects of microstructure on elastic properties of Al2O3/SiC composites

Nanoindentation tests were carried out to investigate certain elastic properties of Al2O3/SiCp composites at microscopic scales (nm up to μm) and under ultra-low loads from 3 mN to 250 mN, with special attention paid to effects caused by SiC particles and pores. The measured Young’s modulus depends on the volume fraction of SiC particles and on the composite porosity and it can compare with that of alumina. The Young’s modulus exhibits large scatters at small penetrations, but it tends to be constant with lesser dispersion as the indentation depth increases. Further analysis indicated that the scatter results from specific microstructural heterogeneities. The measured Young’s moduli are in agreement with predictions, provided the actual role of the microstructure is taken into account.