Delamination growth mechanisms in woven glass fiber reinforced polymer composites under Mode II fatigue loading at cryogenic temperatures

The purpose of this research is to characterize the cryogenic delamination growth behavior in woven glass fiber reinforced polymer (GFRP) composite laminates subjected to Mode II fatigue loading. Mode II fatigue delamination tests were performed at room temperature, liquid nitrogen temperature (77 K) and liquid helium temperature (4 K) using the four-point bend end-notched flexure (4ENF) test method, and the delamination growth rate data for the woven GFRP laminates were obtained. The energy release rate range was determined by the finite element method. Microscopic examinations of the specimen sections and fracture surfaces were also carried out. The present results are discussed to obtain an understanding of the fatigue delamination growth mechanisms in the woven GFRP laminates under Mode II loading at cryogenic temperatures.