Transverse crack growth behavior considering free-edge effect in quasi-isotropic CFRP laminates under high-cycle fatigue loading

The high-cycle fatigue characteristics focused on the behavior of the transverse crack growth up to 108 cycles were investigated using quasi-isotropic carbon fiber reinforced plastic (CFRP) laminates whose stacking sequence was [−45/0/45/90]s. To assess the fatigue behavior in the high-cycle region, fatigue tests were conducted at a frequency of 100 Hz in addition to 5 Hz. In this study, to evaluate quantitative characteristics of the transverse crack growth in the high-cycle region, the energy release rate considering the free-edge effect was calculated. Transverse crack growth behavior was evaluated based on a modified Paris law approach. The results revealed that transverse crack growth was delayed under the test conditions of the applied stress level of σmax/σb = 0.2.