Influence of prepreg conditions on the void occurrence and tensile properties of woven glass fiber-reinforced polyimide composites
Author/Authors :
Tamaki Naganuma، نويسنده , , Kimiyoshi Naito، نويسنده , , Junro Kyono، نويسنده , , Yutaka Kagawa، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2009
Pages :
6
From page :
2428
To page :
2433
Abstract :
The influence of prepreg solvent content on void occurrence in woven glass fiber-reinforced polyimide composites and their tensile properties was studied. A precursor solution of SKYBOND 703 was diluted in an additional solvent (n-methyl pyrrolidone) and the glass woven fabric was immersed in about 40 wt.% polyamic acid, in solvent. Prepregs were dried at 373 K for different time intervals, ranging from 2 to 24 h. Prepregs with varying residual solvent content under each condition were laid up, and their [(0/90)]4 composite laminates were formed by autoclaving at a hydrostatic pressure of 0.7 MPa. The relationship of drying time with the amount of residual prepreg solvent, as well as with the volume fractions of fiber and voids was investigated. The void geography and content for each composite laminate, and the tensile strength and modulus at room temperature were also evaluated. The results clearly indicated that, depending on the altering residual solvent content in the prepreg, the void geometry and location influenced reduction of the tensile properties of woven fabric composite laminate. An appropriate prepreg resin viscosity during curing, which avoids reduction of the tensile properties, was revealed.
Keywords :
A. PMCs , B. Voids , D. Optical microscopy , Polyimide , B. Strength , D. SEM