Improving the flexural and thermomechanical properties of amino-functionalized carbon nanotube/epoxy composites by using a pre-curing treatment Pages 765-771

A prior thermal (pre-curing) treatment of mixtures of epoxy monomer and amino-functionalized carbon nanotubes (CNTs) was used to promote a chemical reaction between the matrix and the reinforcement, favouring the formation of a strong interface. Samples of epoxy resin and different weight percentages of amino-functionalized multi-walled CNTs were prepared with and without the pre-curing treatment (150 °C, 1 h). The degree of dispersion of the nanofiller was better when this pre-curing treatment was used. This allowed a higher CNT content while keeping a high sample homogeneity. Without the pre-curing step, the addition of CNTs increases both the flexural strength and strain to failure by 45%. Moreover, with the pre-curing step, the nanocomposite with 0.25 wt.% CNTs presents an increase of flexural strength by 58% and strain to failure by 68% regard to neat epoxy resin.