YAG:Ce3+ nano-sized particles prepared by precipitation technique

Precipitation process was applied to synthesize cerium-activated YAG using metal nitrates as starting materials. XRD analysis shows that phase-pure phosphors can be obtained at temperatures ∼800 °C and their crystallization enhances with increasing annealing temperature. From SEM and TEM photographs, as-prepared particles are monocrystalline with fine size mostly in the range 40–100 nm. PL peak intensity increased with increasing annealing temperature and decreases with increasing Ce3+ doping concentration. Blue shift occurs as Ce3+ doping concentration increased, according to the increase in crystal field.