Highly toughened polypropylene/ethylene–propylene-diene monomer/zinc dimethacrylate ternary blends prepared via peroxide-induced dynamic vulcanization

Polypropylene (PP)/ethylene–propylene-diene monomer (EPDM)/zinc dimethacrylate (ZDMA) blends with remarkable toughness and extensibility were successfully prepared via peroxide dynamical vulcanization. A unique structure with the EPDM particles surrounded by a transition zone containing numerous polymerized ZDMA (PZDMA) nano-particles was observed for the first time by using transmission electron microscopy (TEM) examination, which contributed to the dramatically increase of Izod impact strength. Dynamic mechanical analysis (DMA) confirmed that the possible PZDMA graft products resulted from peroxide dynamical vulcanization improved the compatibility between EPDM and PP phases. The specific morphology of the PP/EPDM/ZDMA blends indicated that ZDMA can lead to size reduction and good distribution uniformity of the crosslinked rubber particles and the increase of adhesion between PP matrix and EPDM phases during deformation. The synergic effect of the increase in the effective volume of the EPDM phase, the improved compatibility and adhesion between EPDM and PP phases and the deformation of those fine rubber particles is believed to result in the remarkable high toughness and extensibility of the PP/EPDM/ZDMA blends. Particularly for the PP/EPDM ratio of 70/30, the PP/EPDM/ZDMA (70/30/9, w/w/w) ternary blends with the Izod impact strength nearly 2 times higher than PP/EPDM (70/30, w/w) binary blends and 15–20 times higher than PP are achieved; besides, the elongation at break of PP/EPDM/ZDMA ternary blends is 4–5 times higher than that of PP/EPDM binary blends.