Surface morphology and dewettability of self-organized thermosets involving epoxy and POSS-capped poly(ethylene oxide) telechelics

A heptaphenyl polyhedral oligomeric silsesquioxane-capped poly(ethylene oxide) (POSS-capped PEO) telechelics was synthesized via the Huisgen 1,3-dipolar cycloaddition between 3-azidopropylheptaphenyl POSS and α,ω-dialkynyl-terminated poly(ethylene oxide). The organic–inorganic amphiphile was incorporated into epoxy to obtain the organic–inorganic nanocomposites. The morphology of the nanocomposites was investigated by means of atomic force microscopy (AFM) and dynamic mechanical thermal analysis (DMTA). It was found that the epoxy thermosets containing POSS-capped PEO telechelics were microphase-separated. The formation of the nanophases in the thermosets followed a self-assembly mechanism. The static contact angle measurements show that the nanocomposites displayed a significant enhancement in surface hydrophobicity as well as reduction in surface free energy. The improvement in surface dewettability was ascribed to the enrichment of POSS cages at the surface of the nanocomposites and the formation of the specific surface morphology as evidenced by X-ray photoelectron spectroscopy (XPS) and surface atomic force microscopy (AFM).