The effect of annealing temperatures and cooling rates on microstructure and mechanical properties of investment cast Ti–6Al–4V alloy

Production of investment castings of titanium alloys was considerably increased during last years due to the significant cost savings compared to complicated machined parts. However, the disadvantage of as-cast titanium alloys is that the heat-treatment remains only a limited option for improvement of their properties. The object of this paper was to study the effect of heat-treatment of investment cast Ti–6Al–4V alloy performing X-ray diffraction analysis, light microscopy and quantitative metallography together with hardness and room temperature tensile tests. The effect of annealing temperatures (above and below β transus temperature) and cooling rates on microstructure and mechanical properties was discussed in terms of the β → α transformation. The results of this paper also show that, besides heat treatment parameters, melting and casting practice together with mold technology strongly influence the properties of castings.