Microstructure evaluation of Al–Al2O3 composite produced by mechanical alloying method

Mechanical alloying process using ball-milling techniques, has received much attention as a powerful tool for fabrication of several advanced materials, including amorphous, quasicrystals, nanocrystalline and composite materials, etc. This research is focused on production of Al–Al2O3 composite materials by mechanical alloying method and on investigation of its microstructure. For this purpose a horizontal ball mill was designed and manufactured. Aluminum and alumina powders, with specified size and weight percent, were added to the mill. The mixed powders were milled at different times. The milled powders were pressed and sintered under argon gas control. Microstructure of produced composite was investigated by scanning electron microscope. The results show that increasing milling time causes to make fine alumina powders as well as uniform distribution within aluminum, also in steady-state stage increasing milling time has not significant effect on their size distribution within aluminum. The results of atomic analysis of initial and milled powders at different times show that at the beginning of milling, the powders will tend to absorb iron and gradually their susceptibility decrease until steady-state condition is prevailed. The result of infrared spectroscopy does not show any evidence of compounds except alumina.