Influence of surface coating on ballistic performance of aluminum plates subjected to high velocity impact loads

Ballistic response of single or multi-layered metal armor systems subjected to high velocity impact loads was investigated in many experimental, theoretical and numerical studies. In this study, influences of plasma spray surface coating on high velocity impact resistance of AA 6061 T651 aluminum plates were analyzed experimentally. Two different types of surface coating were applied to plates using plasma spray. Using 9.00 mm Parabellum bullets, ballistic performance of both uncoated and coated plates was tested. After the impact tests, penetration depth including plate bending on the front face and bulging on the rear face of the target plate was measured. The improvement on the ballistic resistance of the coated plates was clearly observed. The increase in non-perforating projectile velocity and the decrease in penetration depth were both experienced.