Effects of temperature on tensile and impact behavior of dissimilar welds of rotor steels

Tensile and impact behavior of dissimilar weld joints of newly developed rotor steels 23CrMoNiWV88 and 26NiCrMoV145 were conducted at various temperatures below 350 °C. Inhomogeneous microstructures and asymmetrical micro-hardness along the dissimilar welding joint were observed. With the increase of temperature, strength decreased which was associated with the increased plasticity, and fracture location changed from weld metal (WM) to intermediate pressure (IP) base metal (BM) at around 300 °C. Compared to the homogeneous impact specimen with two fracture zones at fracture surface, a combined quasi-cleavage and ductile fracture mode with three zones is observed at the fracture surface of the dissimilar weld joint when the testing temperature is in the range of 0–40 °C. The occurrence of separated zones are mainly ascribed to the multi-layer welding process and thus improved the impact toughness of the welding joint.