Influence of texture on corrosion rate of AZ31 Mg alloy in 3.5 wt.% NaCl

In this study, AZ31 Mg alloys with different grain orientation were prepared to investigate the influence of texture on corrosion rate in 3.5 wt.% NaCl. Experimental results showed that texture had significant influence on the corrosion rate of AZ31 in 3.5% NaCl. The corrosion rate of AZ31 dramatically increased with the (0 0 0 1) texture intensity decreased and the (1 0 −1 0)/(1 1 −2 0) texture intensity increased. The corrosion rate reached a maximum at about 3 h immersion and subsequently decreased slightly due to the formation of a Mg(OH)2 corrosion product layer. This study indicates that the corrosion rate of AZ31 Mg alloy in NaCl solution can be modified to some extend by controlling texture.