Uniaxial ratcheting behavior of Zircaloy-4 tubes at room temperature

In this study, a series of uniaxial tensile, strain cycling and uniaxial ratcheting tests were conducted at room temperature on Zircaloy-4 (Zr-4) tubes used as nuclear fuel cladding in Pressurized Water Reactors (PWRs) for the purpose to investigate the uniaxial ratcheting behavior of Zr-4 and the factors which may influence it. The experimental results show that at room temperature this material features cyclic softening remarkably within the strain range of 1.6%, and former cycling under larger strain amplitude cannot retard cyclic softening of later cycling under lower strain amplitude. Uniaxial ratcheting strain accumulates in the direction of mean stress, and the ratcheting stain level is larger under tensile mean stress than that under compressive mean stress. Uniaxial ratcheting strain level increases with the increase of mean stress and stress amplitude, and decreases with the increase of loading rate. The sequence of loading rate appears to have no effects on the final ratcheting strain accumulation. Loading history has great influence on the uniaxial ratcheting behavior. Lower stress level after loading history with higher stress level leads to the shakedown of ratcheting. Higher loading rate after loading history with lower loading rate brings down the ratcheting strain rate. Uniaxial ratcheting behavior is sensitive to compressive pre-strain, and the decay rate of the ratcheting strain rate is slowed down by pre-compression.