Optimization of geometrical characteristics of perforated plates

In this paper, an attempt was made to design effective non-homogenous armor in form of perforated plate mounted at close distance from basic armor plate. Perforated plate with three perforation diameters: 9, 10 and 11 mm, two ligaments length: 3.5 and 4.5 mm ligaments, set at 0° and 28° angles, were combined to 13 mm basic plate and tested against 12.7 mm API ammunition. It has been shown that larger perforations gave a more efficient core fragmentation, while angled specimens were the only ones that offer full protection against five API shots when the perforated plate was placed at 100 mm from the basic plate. Perforations that are similar in size to the penetrating core diameter offer a more efficient core fracture, leading to a faster fragment separation. This may enable a smaller distance between the add-on perforated and basic plate to be used. Scanning electron microscopy analysis has shown a ductile fracture mode at impact point, with hardness values on plate basic level. On the other hand, a brittle fracture mode with a rise in local hardness measured near impact point is a result of intensive high speed plastic deformation produced by bending stresses. A drop in local hardness measured near impact point, may be the result of intensive cracking that occur due to repeated projectile impact.