Effects of initial grain size on hot deformation behavior of commercial pure aluminum

The effects of initial grain size of commercial pure aluminum on hot deformation behavior were investigated using hot compression tests. The hot compression tests were carried out on the pure aluminum samples with the initial grain sizes of 50, 150 and 450 μm using various strains, strain rates and different deformation temperatures. It was found that the hot deformation behavior of used material was sensitive to deformation conditions and initial microstructure. Results indicate that the initial grain size has significant effect on the flow stress. Flow stress decreases when the grain size decreases from 450 to 50 μm and when strain rate is lower than 0.05 s−1. This procedure is reversed at strain rate of 0.5 s−1. Furthermore, effects of other parameters like the strain rates and deformation temperatures on the flow stresses and hardening rates were investigated. It was also found that the inhomogeneity of microstructure distribution at different positions of the deformed specimens depended on the amount of deformation concentration at particular points and other processing parameters such as initial grain sizes, strain rates and deformation temperatures. In addition the geometric dynamic recrystallization (GDRX) was observed in the specimens highly strained (0.7) at elevated temperature (500 °C) using polarized light microscope and sensitive tint (PLM + ST).