Preparation and pore control of highly mesoporous carbon from defluorinated PTFE Original Research Article

Porous carbon having more than 2000 m2/g of BET specific surface area was synthesized by defluorination of polytetrafluoroethylene (PTFE) at 473 K using sodium metal. The porous carbon as-prepared had a large amount of narrow mesopores 2–3 nm in pore width, together with micropores. Control of the pore structure was attempted by simple heat-treatment of the carbon in nitrogen, and change of the porous structures was characterized by nitrogen adsorption techniques. As a result, it was found that the ratio between micro- and mesopores was easily varied. Electric double layer capacitance was measured as one of the applications for the mesoporous carbon with specific porosity, and the effect of pore control on capacitance was investigated.