Influence of activated carbon pore structure on oxygen reduction at catalyst layers supported on rotating disk electrodes Original Research Article

Carbon materials are often used as catalyst supports, and for catalysts in electrodes of a polymer electrolyte fuel cell, carbon black has been used. Recently, it was found, however, that activated carbon could replace carbon black and besides, significantly improve the activity of the electrode catalyst layer for oxygen reduction. In the present study, to optimize the pore structure of activated carbon for further activity improvement, the influence of the pore structure on the activity was investigated using activated carbon of various specific surface areas and mean pore diameters. A catalyst layer was formed from activated carbon loaded with platinum and a polymer electrolyte. The activity of the layer was measured in an oxygen-saturated perchloric acid solution, supporting the layer on a rotating glassy carbon disk electrode. We found that increases in the specific surface area and mean pore diameter increased the activity and that the latter was more effective than the former mainly due to the enhanced mass-transfer in the pores; the catalyst layer formed from activated carbon with the largest mean pore diameter was the most active. Unless pores excessively develop and lose connections between particles, a large pore diameter is therefore desired for the fuel cell electrodes.