Simple synthesis of mesoporous carbon with magnetic nanoparticles embedded in carbon rods Original Research Article

Magnetically separable ordered mesoporous carbon containing magnetic nanoparticles embedded in the carbon walls was synthesized using a simple synthetic procedure. The resulting magnetically separable mesoporous carbon was denoted as M-OMC (magnetically separable ordered mesoporous carbon) poly(pyrrole) with residual Fe2+ ions in the mesoporous channel was converted to carbon material containing superparamagnetic nanoparticles. The size of the magnetic nanoparticles obtained was restricted by the channel size of the SBA-15 silica template, which resulted in the generation of superparamagnetic nanoparticles embedded in the carbon rods. The blocking temperature of M-OMC is 110 K. Pore size and textural property of M-OMC is similar to that of hexagonally ordered mesoporous carbon fabricated using SBA-15 silica as a template. The saturation magnetization of M-OMC is ca. 30.0 emu/g at 300 K, high enough for magnetic separation.