Methane sorption on ordered mesoporous carbon in the presence of water Original Research Article

An ordered mesoporous carbon was synthesized using SBA-15 as the template. The sorption isotherms of methane on the synthesized carbon material were collected. Its ordered structure was confirmed by the XRD, SEM and TEM examinations. The BET surface area is 1100–1200 m2/g, the total pore volume is 1.24–1.30 cm3/g, and the pore size distribution is very narrow and centered at 2–5 nm. As high as 41.2 wt.% of methane was stored per unit mass of carbon at 275 K and pressures less than 7 MPa in the presence of 3.86 times more water. This sorption amount is 31% higher than the largest sorption capacity reached by activated carbon in the presence of water, which was equal to or higher than the storage capacity of compression till 20 MPa. The enthalpy change corresponding to the sudden change of isotherms was equal to the enthalpy change of methane hydrate formation; therefore, the mechanism of the enhanced methane storage was considered due to the formation of methane hydrate in the porous carbon material.