Increasing the toughness of nylon 12 by the incorporation of functionalized graphene Original Research Article

The effect of functionalized graphene (FG) on the mechanical properties, especially toughness, of nylon12 was investigated. The results revealed that the incorporation of a very small amount (about 0.6 wt%) of the FG caused a significant improvement in ultimate tensile strength, elongation, impact strength and toughness. With 0.6 wt% FG ultimate tensile strength and elongation at break of the nylon 12 are improved by ∼35% and ∼200%, respectively. The KIc of the nylon 12 is ∼1.28 MPa m0.5 and the incorporation of 0.6 wt% FG causes a significant increase of 72% (∼2.2 MPa m0.5). 0.6 wt% FG also causes a significant improvement of 175% in impact failure energy of the nylon 12. The incorporation of FG resulted in an increase in amount of γ-phase of nylon12 which could be the direct reason for the increase of toughness.