Tuning the compressive mechanical properties of carbon nanotube foam Original Research Article

A post-growth chemical vapor deposition (CVD) treatment was used to tune the compressive mechanical properties of carbon nanotube (CNT) arrays. Millimeter tall CNT arrays with low compressive resilience were changed to a foam-like material with high compressive strength and almost complete recovery upon unloading. The foam was tuned to provide a range of compressive properties for various applications. The treated arrays demonstrated compressive strength up to 35× greater than the as-grown CNT array. Unlike polymeric foams, the CNT foam did not decompose after exposure to high temperatures. Investigation of the foam structure revealed that the CVD treatment increased CNT diameter through radial growth, while increasing the CNT surface roughness. The morphological changes help to explain the increase in CNT array compressive strength and the transition from permanent array deformation to foam-like recovery after compressive loading.