Oxidation protection of C/C composites with a multilayer coating of SiC and Si + SiC + SiC nanowires Original Research Article

An oxidation protective Si–SiC coating with randomly oriented SiC nanowires was prepared on the SiC-coated carbon/carbon (C/C) composites by a two-step technique. First, a porous network of SiC nanowires was produced using chemical vapor deposition. This material was subjected to pack cementation to infiltrate the porous layer with a mixture of Si and SiC. The nanowires in the coating could efficiently suppress the cracking of the coating by various toughening mechanisms including nanowire pullout, nanowire bridging, microcrack deflection and good interaction between nanowire/matrix interface. The results of thermogravimetric analysis and thermal shock showed that the coating had excellent oxidation protection for C/C composites between room temperature and 1500 °C. These results were confirmed by two additional oxidation experiments conducted at temperature of 900 and 1400 °C, which demonstrated that the coating could efficiently protect C/C composites from oxidation at 900 °C for more than 313 h or at 1400 °C for more than 112 h.