R-curve behavior of BaTiO3- and PZT ceramics under the influence of an electric field applied parallel to the crack front Original Research Article

The fracture resistance curves (R-curves) of BaTiO3 and commercial PZT–PIC 151 were measured with compact tension specimens under the influence of an electric field applied parallel to the crack front. A strong influence of the electric field on the starting and plateau value was found as well as on the length of the R-curve. Generally a toughness increase was detected with increasing electric field. The toughening effect is estimated from the change in crack tip stress intensity induced by ferroelastic domain switching near the crack tip using the weight function formalism developed for stress-induced transformation toughening of zirconia ceramics. In order to obtain a quantitative prediction of toughening, ferroelastic and ferroelectric properties were measured.