Glass-forming ability and thermal stability of Nd70−xFe20Al10Yx alloys Original Research Article

The glass-forming ability (GFA) and thermal stability of Nd70−xFe20Al10Yx (0≤x≤15) alloys produced by melt spinning and copper-mold casting have been investigated. Ribbon samples in the composition range show a fully amorphous structure. Except Y=5 at.%, bulk amorphous alloys at least 2 mm in diameter were obtained. Both the amorphous ribbon and the bulk cylinder for the Nd55Fe20Al10Y15 alloy show a distinct glass transition temperature and a wide supercooled liquid region before crystallization. It is suggested to use a new parameter to characterize both the GFA and the thermal stability of Nd–Fe–Al–Y alloys, showing that Nd60Fe20Al10Y10 alloy is the best one both in GFA and thermal stability. The remanence (Jr), magnetization (J1500), and coercivity (Hc) for the as-cast Nd70−xFe20Al10Yx amorphous cylinders depend strongly on the composition. The enhanced GFA and thermal stability as well as the reduction of magnetic properties are discussed.