Texture analysis of a friction stir processed 6061-T6 aluminum alloy using neutron diffraction Original Research Article

Time-of-flight neutron diffraction was used to investigate the texture changes in friction stir-processed (FSP) 6061-T6 aluminum alloy plates. Two different specimens were prepared with the purpose of separating the effects of frictional heating and severe plastic deformation on the changes of the preferred orientation in the as-received rolled plates: a plate processed with both stirring pin and tool shoulder, i.e., a regular FSP plate subjected to both severe plastic deformation and frictional heating (Case 1); and a plate processed only with the tool shoulder, i.e., subjected mainly to frictional heating (Case 2). The diffraction peak intensities provide insights into the texture variations at various locations across the centerline and through the thickness of the FSP plates. Comparison of the texture variations between Cases 1 and 2 clearly shows that the severe plastic deformation from the stirring pin affects the preferred orientation during the FSP, while heating alone from the tool shoulder has little effect.