Partial dislocation configurations in a low-angle boundary in α-Al2O3 Original Research Article

The dislocation structures of a low-angle tilt grain boundary in alumina bicrystal were investigated by transmission electron microscopy. The grain boundary was found to consist of two regions: an area with pairs of partial dislocations and an area with groups of odd numbered partial dislocations (multiple-partial-structure). Eight kinds of multiple-partial-structures were found in the fabricated grain boundary. The Burgers vectors of each partial dislocation in the grain boundary can be distinguished by dark-field imaging, and thus the arrangement of partial dislocations in the multiple-partial-structures are determined. It is concluded that a slight twist component of the boundary is the origin of the characteristic multiple-partial-structures.