Wear and friction of TiAlN/VN coatings against Al2O3 in air at room and elevated temperatures Original Research Article

TiAlN/VN multilayer coatings exhibit excellent dry sliding wear resistance and low friction coefficient, reported to be associated with the formation of self-lubricating V2O5. To investigate this hypothesis, dry sliding ball-on-disc wear tests of TiAlN/VN coatings on flat stainless steel substrates were undertaken against Al2O3 at 25 °C, 300 °C and 635 °C in air. The coating exhibited increased wear rate with temperature. The friction coefficient was 0.53 at 25 °C, which increased to 1.03 at 300 °C and decreased to 0.46 at 635 °C. Detailed investigation of the worn surfaces was undertaken using site-specific transmission electron microscopy (TEM) via focused ion beam (FIB) microscopy, along with Fourier transform infrared (FTIR) and Raman spectroscopy. Microstructure and tribo-induced chemical reactions at these temperatures were correlated with the coating’s wear and friction behaviour. The friction behaviour at room temperature is attributed to the presence of a thin hydrated tribofilm and the presence of V2O5 at high temperature.