Interdependent effect of chemical composition and thermal history on artificial aging of AA6061 Original Research Article

In this study, the interdependent effect of chemical composition and thermal history on artificial aging was investigated for the aluminum alloy AA6061. Based on thermodynamic calculations, including Al, Fe, Cr, Zn, Ti, Mg, Si and Cu, model alloys exhibiting a maximum variation of the reachable solute super-saturation of elements relevant for precipitation hardening within the compositional limits of AA6061 were produced. The artificial aging behavior of these alloys at 175 °C was studied by tensile testing for two thermal histories, including very short- and long-term room temperature storage after quenching. Precipitation during artificial aging was investigated by an analysis of yield strength data. As generally expected, precipitation kinetics was found to depend strongly on the solute super-saturation in the case of very short room temperature storage. For artificial aging after long-term room temperature storage the kinetics showed almost no dependence on the chemical composition. This seems to be an exception from simple precipitation kinetics and can be explained based on the complex role of quenched-in vacancies in artificial aging of AA6061.