ω Transformation in cold-worked Ti–Nb–Ta–Zr–O alloys with low body-centered cubic phase stability and its correlation with their elastic properties Original Research Article

The ω transformation and its correlation with elastic properties were investigated in cold-worked Ti–36Nb–2Ta–3Zr–xO mass% alloys with low body-centered cubic (β) phase stability, known as gum metal. Analysis of the temperature dependence of the ω (hexagonal) phase formation using transmission electron microscopy and of the elastic properties of solution-treated and cold-worked alloys using resonant ultrasound spectroscopy revealed that in the solution-treated 0.36% and 0.51% O alloys, the high concentration of oxygen suppressed ω-phase formation from room temperature to a fairly low temperature of ∼13 K. However, the ω phase was formed by cold working at room temperature in the 0.30% and 0.47% O alloys. Importantly, the fraction of the ω phase clearly increased upon cooling, which indicates that the formation of the ω phase is thermodynamically favorable near and below room temperature in the cold-worked 0.30% and 0.47% O alloys. This formation of the ω phase and the low stability of the β phase related to the low electron/atom (e/a) ratio were the dominant factors determining the elastic properties near and below room temperature in the cold-worked Ti–Nb–Ta–Zr–O alloys.