Gold catalysts supported on mesoporous titania for low-temperature water–gas shift reaction Original Research Article

Mesoporous titania with high surface area and uniform pore size distribution was synthesized using surfactant templating method through a neutral [C13(EO)6–Ti(OC3H7)4] assembly pathway. The different gold content (1–5 wt.%) was supported on the mesoporous titania by deposition–precipitation (DP) method. The catalysts were characterized by X-ray diffraction, TEM, SEM, N2 adsorption analysis and TPR. The catalytic activity of gold supported mesoporous titania was evaluated for the first time in water–gas shift reaction (WGSR). The influence of gold content and particle size on the catalytic performance was investigated. The catalytic activity was tested at a wide temperature range (140–300 °C) and at different space velocities and H2O/CO ratios. It is clearly revealed that the mesoporous titania is of much interest as potential support for gold-based catalyst. The gold/mesoporous titania catalytic system is found to be effective catalyst for WGSR.