Molecule Derived Synthesis of Nanocrystalline YFeO3 and Investigations on Its Weak Ferromagnetic Behavior

new Y-Fe alkoxide, [YFe(OPri)6(PriOH)]2, is used in the sol-gel process to obtain the orthoferrite, YFeO3. The Y/Fe stoichiometry (1:1) and Y-O(R)-Fe chemical links in the single molecular precursor kinetically control the formation of metastable YFeO3 which is otherwise difficult to prepare due to the easy formation of the garnet composition, Y3Fe5O12. TG/DTA analysis showed the crystallization of YFeO3 at 680 C, which was confirmed by XRD data. The powders obtained were nanocrystalline (TEM) and the only crystalline compound present between 600 and 1300 C was monophasic YFeO3. The absence of garnet and other iron-containing residual phases observed in previous studies was confirmed by temperature-dependent Mussbauer and magnetization measurements. The magnetization data support a weak ferromagnetic behavior and reveal lowand high-field regimes in M-T and M-H curves, corresponding to magnetocrystalline and antisymmetric -exchange anisotropy, respectively.