Synthesis and Characterization of Stable and Crystalline Ce1-xZrxO2 Nanoparticle Sols

Ce1-xZrxO2 nanoparticle sols (x = 0-1) are synthesized by hydroxide coprecipitation of a mixed precursor solution of cerium ammonium nitrate and zirconyl chloride followed by redispersion in an aqueous medium by sonication using nitric acid as the peptizing agent. The obtained sols are highly concentrated and stable for weeks. Analytical ultracentrifugation measurements show a particularly narrow particle distribution with an average particle size of about 3.5 nm for pure CeO2 and 2.5 nm for pure ZrO2 nanoparticles. Wide-angle X-ray scattering (XRD) as well as high-resolution transmission electron microscopy give evidence that all of the assynthesized nanoparticle sols with a ceria content larger than 20 mol % are well crystalline. The formation of a solid solution with an increasing amount of Zr was monitored by XRD and Raman spectroscopy.