The effect of cold expansion on fatigue crack growth from open holes at room and high temperature

In this paper a series of residual stress measurements and fatigue crack growth tests have been carried out using aluminium alloy 2650 specimens containing cold expanded and non cold expanded holes. Residual stress measurements have been done after cold expansion and after various loading and temperature conditions. In order to measure an angular variation of residual stresses, X-ray and a new technique called the Garcia–Sachs method have been employed. Results revealed that residual stress relaxation occurred as a result of exposure at 150°C. The magnitude of relaxation was shown to be dependent on the level and the sign of externally applied load. Fatigue crack growth tests have been carried out at 20°C and 150°C for both cold expanded and non-cold expanded conditions. Fatigue crack growth rates in specimens containing cold expanded fastener holes were affected significantly by elevated temperature exposure. Depending on the exposure time and loading conditions the fatigue life improvement was found to be between one and greater than 10 for tests at 20°C.