A two parameter driving force for fatigue crack growth analysis

A model for fatigue crack growth (FCG) analysis based on the elastic–plastic crack tip stress–strain history was proposed. The fatigue crack growth was predicted by simulating the stress–strain response in the material volume adjacent to the crack tip and estimating the accumulated fatigue damage. The fatigue crack growth was regarded as a process of successive crack re-initiation in the crack tip region. The model was developed to predict the effect of the mean stress including the influence of the applied compressive stress. A fatigue crack growth expression was derived using both the plane strain and plane stress state assumption. It was found that the FCG was controlled by a two parameter driving force in the form of: image. The driving force was derived on the basis of the local stresses and strains at the crack tip using the Smith–Watson–Topper (SWT) fatigue damage parameter: D=σmaxΔε/2.The effect of the internal (residual) stress induced by the reversed cyclic plasticity was accounted for the subsequent analysis. Experimental fatigue crack growth data sets for two aluminum alloys (7075-T6 and 2024-T351) and one steel alloy (4340) were used for the verification of the model.