Enhanced fatigue behavior of a glass fiber reinforced hybrid particles modified epoxy nanocomposite under WISPERX spectrum load sequence

Two types of glass fiber reinforced plastic (GFRP) composites were fabricated viz., GFRP with neat epoxy matrix (GFRP-neat) and GFRP with hybrid modified epoxy matrix (GFRP-hybrid) containing 9 wt.% of rubber microparticles and 10 wt.% of silica nanoparticles. Fatigue tests were conducted on both the composites under WISPERX load sequence. The fatigue life of the GFRP-hybrid composite was about 4–5 times higher than that of GFRP-neat composite. The underlying mechanisms for improved fatigue performance are discussed. A reasonably good correlation was observed between the experimental fatigue life and the fatigue life predicted under spectrum loads.