Uniaxial tensile behaviour of ZM-21 magnesium alloy at room temperature

Experiments were carried out to generate data on the uniaxial tensile forming of hot rolled ZM-21 magnesium alloy using a Hounsefield tensometer. During the experimental investigation at three different orientations namely rolling, transverse and thickness directions, the magnesium alloy was found to show increase in flow stress with respect to increasing amount of axial strain or deformation. Further, it was noted that the strain hardening index value for the thickness direction beyond the axial strain value of 0.08 is high while comparing the results obtained from other two directions. The plastic strain ratio value for directions namely rolling and transverse was observed to be very high for low strain value (less than strain value of 0.02) and low for high strain value. The ratio of true stress value at rolling direction to the true stress value at transverse direction was almost the same up to the axial strain value of 0.06 and then decreased with increasing axial strain value.