The indirect ultrasonic vibration process for rheo-squeeze casting of A356 aluminum alloy

The semisolid slurry of A356 Al alloy was prepared by indirect ultrasonic vibration (IUV) method and then formed by direct squeeze casting (SC). The effects of squeeze pressure and T6 heat treatment on the microstructure and mechanical properties of rheo-squeeze casting (RSC) A356 Al alloy were investigated. The results indicate that with the increase of squeeze pressure, the average diameter of primary α-Al particles decreased, while the densities and mechanical properties of the samples increased. The effect of T6 heat treatment on the mechanical properties is more significant in RSC samples than in conventional SC samples. The tensile strength and elongation of T6 heat treated RSC samples under 100 MPa pressure are 338 MPa and 8%, respectively.