Reactivity in the solid state between CoWO4 and RE2WO6 where RE = Sm, Eu, Gd

Reactivity in the solid state between CoWO4 and some rare-earth metal tungstates RE2WO6 (RE = Sm, Eu, Gd) was investigated by the XRD method. Two families of new isostructural cobalt and rare-earth metal tungstates, Co2RE2W3O14 and CoRE4W3O16, were synthesized. The Co2RE2W3O14 phases are formed by heating in air the CoWO4 and RE2WO6 compounds mixed at the molar ratio 2:1, while the CoRE4W3O16 phases are synthesized at the molar ratio of CoWO4/RE2WO6 equals to 1:2. The Co2RE2W3O14 phases as well as the CoRE4W3O16 compounds crystallize in the orthorhombic system. The Co2RE2W3O14 and CoRE4W3O16 compound melt above 1150 °C. A melting manner of the Co2RE2W3O14 and CoRE4W3O16 compounds was determined in an inert atmosphere. The formation of CoWO4−x phase was observed during heating in an inert atmosphere.