Physical ageing and molecular mobilities of sulfonated polysulfone for proton exchange membranes

The thermal behaviour, the physical ageing and the amorphous phase dynamics of polysulfone (PSU) and sulfonated polysulfone (SPSU) are characterized by thermogravimetric analysis and temperature modulated differential scanning calorimetry. The sulfonic group introduction (the sulfonation degree is 70%) in the polymer implies a drastic decrease of the thermal decomposition temperature (220 and 517 °C for SPSU and PSU respectively) and a modification of calorimetric parameters (for SPSU, the heat capacity in the glassy state is lower and the glass transition temperature Tg is higher than for PSU). In terms of molecular dynamics, the amorphous phase heterogeneities are greater and the cooperative rearranging region size at the glass transition temperature is smaller for SPSU than for PSU. Moreover, after a physical ageing process, the enthalpy recovery kinetic has slowed down by sulfonation. These results can be explained from the existence of sulfonic domains confining the amorphous phase domains.