Thermal stability and oxidizing properties of mixed alkaline earth-alkali molten carbonates: A focus on the lithium-sodium carbonate eutectic system with magnesium additions

A comparative study on thermal behavior and oxygen solubility properties of eutectic 52/48 lithium/sodium carbonate salt containing minor additions of magnesium up to 10 mol% has been made in order to determine whether a general correlation between these two properties can be found or not. Consecutive TG/DSC heating/cooling thermal cycles carried out under alternating CO2 and N2 gas flows allowed to assign thermal events observed in the premelting region to a partial decarbonation process of the magnesium-alkali mixed carbonates. The observed decarbonation process at 460 °C is believed to come from initial stage of thermal decomposition of magnesium carbonate resulting in the metastable formation of magnesium oxycarbonate-like phases MgO·2MgCO3, in a similar manner as previously reported for lanthanum. Reversible formation and decomposition of the magnesium carbonate phase has been observed under a CO2 gas atmosphere. The intensity of the decomposition process shows a maximum for a 3 mol% MgO addition that gives also the highest oxygen solubility, suggesting therefore that instability thermal analysis in the premelting region can be considered as providing an effective measure of the basicity/oxidizing properties of alkali carbonate melts with magnesium or, in more general terms, with cations that are strong modifiers of the carbonate melt basicity through formation of soluble oxycarbonate phases.